We will make every effort to be outstanding and perfect, and accelerate our steps for standing in the rank of international top-grade and high-tech enterprises for Aggse Crystal, Yb Yag Crystal, Kd P Eo Q-Switch, We have four leading products. Our products are best sold not only in the Chinese market, but also welcomed in the international market.

Short Lead Time for Lutetium Aluminium Garnet Doped With Praseodymium - Co:Spinel Crystals – Dien Detail:

Passive Q-switches or saturable absorbers generate high power laser pulses without the use of electro-optic Q-switches, thereby reducing the package size and eliminating a high voltage power supply. Co2+:MgAl2O4 is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6μm, in particular, for eye-safe 1.54μm Er:glass laser, but also works at 1.44μm and 1.34μm laser wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode laser pumping. Negligible excited-state absorption results in high contrast ratio of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.

Features

• Suitable for 1540 nm eye-safe lasers
• High absorption section
• Negligible excited state absorption
• High optical quality
• Uniformly distributed Co

Applications

• Eye-safe 1540 nm Er:glass laser
• 1440 nm laser
• 1340 nm laser
• Eye-safe laser range finder

Basic Properties

Chemical formula	Co²⁺:MgAl₂O₄
Crystal structure	Cubic
Lattice parameters	8.07Å
Density	3.62 g/cm³
Melting Point	2105°C
Refractive Index	n=1.6948 @1.54 µm
Thermal Conductivity /(W·cm^-1·K^-1@25°C)	0.033W
Specific Heat/ (J·g^-1·K^-1)	1.046
Thermal Expansion /（10^-6 /°C@25°C ）	5.9
Hardness (Mohs)	8.2
Extinction Ratio	25dB
Orientation	[100] or [111] < ±0.5°
Optical density	0.1-0.9
Damage Threshold	>500 MW/cm²
Doping concentration of Co²⁺	0.01-0.3 atm%
Absorption coefficient	0 ～ 7 cm^-1
Working wavelength	1200 – 1600 nm
Coatings	AR/AR@1540，R<0.2%; AR/AR@1340，R<0.2%

Technical Parameters

Orientation Tolerence	< 0.5°
Thickness/Diameter Tolerance	±0.05 mm
Surface Flatness	<λ/8@632 nm
Wavefront Distortion	<λ/4@632 nm
Surface Quality	10/5
Parallel	10〞
Perpendicular	5ˊ
Clear Aperture	>90%
Chamfer	<0.1×45°
Maximum dimensions	Dia(3-15)×(3-50)mm

Product detail pictures:

Related Product Guide:

Every member from our high efficiency sales team values customers' needs and business communication for Short Lead Time for Lutetium Aluminium Garnet Doped With Praseodymium - Co:Spinel Crystals – Dien , The product will supply to all over the world, such as: Manila, Lyon, Bogota, Our mission is "Provide Goods with Reliable Quality and Reasonable Prices". We welcome customers from every corner of the world to contact us for future business relationships and achieving mutual success!

Staff is skilled, well-equipped, process is specification, products meet the requirements and delivery is guaranteed, a best partner!