Low MOQ for Nd Yag 1064 Nm - BBO crystal – Dien


Product Detail

Related Video

Feedback (2)

Adhering into the basic principle of "quality, assistance, effectiveness and growth", we have attained trusts and praises from domestic and worldwide client for 3-5um, Windows For Infrared Band, Fs Crystal, Welcome your enquiry, greatest service is going to be provided with full heart.
Low MOQ for Nd Yag 1064 Nm - BBO crystal – Dien Detail:

High-quality crystals of BGSe (BaGa4Se7) is the selenide analogue of the chalcogenide compound BaGa4S7, whose acentric orthorhombic structure was identified in 1983 and the IR NLO effect was reported in 2009, is a newly developed IR NLO crystal. It was obtained via the Bridgman–Stockbarger technique. This crystal exhibits high transmittance over the wide range of 0.47–18 μm, except for an absorption peak at around 15 μm.
The FWHM of the (002) peak rocking curve is about 0.008° and the transmittance through a polished 2 mm thick (001) plate is around 65% over the wide range of 1–14 μm. Various thermophysical properties were measured on crystals.
The thermal expansion behavior in BaGa4Se7 does not exhibit strong anisotropy with αa=9.24×10−6 K−1, αb=10.76×10−6 K−1, and αc=11.70×10−6 K−1 along the three crystallographic axes. The thermal diffusivity/thermal conductivity coefficients measured at 298 K are 0.50(2) mm2 s−1/0.74(3) W m−1 K−1, 0.42(3) mm2 s−1/0.64(4) W m−1 K−1, 0.38(2) mm2 s−1/0.56(4) W m−1 K−1, along the a, b, c crystallographic axis respectively.
In addition, the surface laser damage threshold was measured to be 557 MW/cm2 using a Nd:YAG (1.064 μm) laser under conditions of 5 ns pulse width, 1 Hz frequency, and D=0.4 mm spot size.
BGSe (BaGa4Se7) crystal exhibits a powder second harmonic generation (SHG) response that is approximately 2–3 times that of AgGaS2. The surface laser damage threshold is about 3.7 times that of AgGaS2 crystal under identical conditions.
BGSe crystal has a large nonlinear susceptibility, and may have a broad prospect for practical applications in the mid-IR spectral region.It shows interesting terahertz phonon-polaritons and high nonlinear coefficients for terahertz generation.
Advantages for IR laser output:
Suitable for various pumping source (1-3μm)
Wide tunable IR output range (3-18μm)
OPA, OPO, DFG, intracavity/extravity, cw/pulse pumping
Important notice: Since this this a new type crystal, inside crystal may have few streaks, but we do not accept returnment due to this defect.


Product detail pictures:

Low MOQ for Nd Yag 1064 Nm - BBO crystal – Dien detail pictures

Low MOQ for Nd Yag 1064 Nm - BBO crystal – Dien detail pictures

Low MOQ for Nd Yag 1064 Nm - BBO crystal – Dien detail pictures

Low MOQ for Nd Yag 1064 Nm - BBO crystal – Dien detail pictures


Related Product Guide:

Our firm aims to operating faithfully, serving to all of our shoppers , and working in new technology and new machine regularly for Low MOQ for Nd Yag 1064 Nm - BBO crystal – Dien , The product will supply to all over the world, such as: Malawi, Madras, Ghana, Our company's main products are widely used all over the world; 80% of our products exported to the United States, Japan, Europe and other markets. All stuff sincerely welcome guests come to visit our factory.
Wide range, good quality, reasonable prices and good service, advanced equipment, excellent talents and continuously strengthened technology forces,a nice business partner.
5 Stars By Elvira from South Korea - 2017.06.16 18:23
The company has rich resources, advanced machinery, experienced workers and excellent services, hope you keep improving and perfecting your products and service, wish you better!
5 Stars By Edwina from Provence - 2017.10.13 10:47